apilon 52® TCLE 25
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | API SpA |
| Trademark: | apilon 52® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8VfNCX_apilon-52-TCLE-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
apilon 52®TCLE 25 is a thermoplastic polyurethane elastomer (polyether)(TPU-polyether) product,. It can be processed by extrusion or injection molding and is available in Europe. apilon 52®The application areas of TCLE 25 include engineering/industrial accessories, electrical/electronic applications, electrical appliances, tools and home applications. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 15 seconds | 81 | ASTM D2240 | |
| Shaw D, 3 seconds | 31 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 22.0 | MPa | ASTM D638 |
| 100% strain | 3.50 | MPa | ASTM D638 |
| 300% strain | 6.00 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Abrasion Resistance | 50.0 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 55.0 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-20°C) | No Break | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 110 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 180 - 190 | °C | |
| Middle Temperature | 185 - 200 | °C | |
| Front Temperature | 190 - 215 | °C | |
| Nozzle Temperature | 200 - 230 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Back Pressure: Medium to LowLocking Pressure: High |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 110 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Cylinder Zone 1 Temp. | 160 - 185 | °C | |
| Cylinder Zone 2 Temp. | 170 - 200 | °C | |
| Cylinder Zone 3 Temp. | 175 - 210 | °C | |
| Cylinder Zone 4 Temp. | 180 - 220 | °C | |
| Die Temperature | 170 - 210 | °C |
| Extrusion instructions |
|---|
| L/D Ratio: 20:1 to 30:1Compression Ratio: 1:2.5 to 1:3 |
| Note Message | |
|---|---|
| 1 . | Without Notch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PA66 2006/274 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Multiuse Leostomer® LJ-3150N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| BLUESTAR® PBT 203G30 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| 3M™ Dyneon™ PTFE Compound TF 4212 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| PENTAMID B MK15 E H black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |