TRIBOFORCE® PPS C1800
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LEIS Polytechnik - polymere Werkstoffe GmbH |
| Trademark: | TRIBOFORCE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8UBOYT_TRIBOFORCE-PPS-C1800.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| polyphenylene sulfide, carbon fibre reinforced, wear and friction modified |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.050 to 0.20 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16000 | MPa | ISO 527-2 |
| Tensile Stress | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2 |
| Coefficient of Friction | ASTM G137 | ||
| vs. Steel - Dynamic 2 | 0.19 | ||
| vs. Steel - Dynamic 3 | 0.29 | ||
| Wear Factor 4 | ASTM G137 | ||
| 3.0 MPa, 1.0 m/sec | 70 | 10^-8 mm³/N·m | |
| 5.0 MPa, 1.0 m/sec | 170 | 10^-8 mm³/N·m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 15 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 275 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.1E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 4.5E-5 | cm/cm/°C |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Temperature of Use - Long-Time | |||
| < 130°C | Yes | ||
| 130 to 200°C | Yes | ||
| 200 to 260°C | No | ||
| 260 to 300°C | No |
| Note Message | |
|---|---|
| 1 . | 60mm x 60mm x 2mm |
| 2 . | 5 MPa, 1 m/s, dry |
| 3 . | 3 MPa, 1 m/s, dry |
| 4 . | Steel |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 GB 20 | RTP Company | PP, Unspecified | RTP |
| Clariant Nylon 6/6 PA-111 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| LNP™ STAT-KON™ PD000 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |
| LNP™ THERMOCOMP™ EX93452 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| OxyVinyls® 155F | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |