ULTEM™ AUT210 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8TPmzC_ULTEMAUT210resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent Polyetherimide (Tg 227 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 212 degC (SABIC IP method). Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 11 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3590 | MPa | ASTM D638 |
| -- | 3320 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 105 | MPa | ASTM D638 |
| Yield | 103 | MPa | ISO 527-2/5 |
| Fracture 3 | 88.0 | MPa | ASTM D638 |
| Fracture | 88.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 8.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/5 |
| Fracture 5 | 75 | % | ASTM D638 |
| Fracture | 54 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3330 | MPa | ASTM D790 |
| -- 7 | 3140 | MPa | ISO 178 |
| Flexural Strength 8(Yield, 50.0 mm Span) | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 38 | J/m | ASTM D256 |
| 23°C | 37 | J/m | ASTM D256 |
| -30°C 10 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2400 | J/m | ASTM D4812 |
| -30°C 12 | No Break | ISO 180/1U | |
| 23°C 13 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 33.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 215 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 201 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 211 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 14 | 196 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 222 | °C | ASTM D1525 15 |
| -- | 221 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 150°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 150°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Metallized Haze Onset | 212 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 360 - 382 | °C | |
| Middle Temperature | 371 - 393 | °C | |
| Front Temperature | 382 - 404 | °C | |
| Nozzle Temperature | 377 - 399 | °C | |
| Processing (Melt) Temp | 382 - 404 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 120*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1373 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Shuman PC SP980 | Shuman Plastics, Inc. | PC | Shuman PC |
| Chemlon® MDF30 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Karina LILAC 2563U -E TR-600N34/189-YT-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom BB 73 F C12463 | LyondellBasell Industries | PP Copolymer | Hostacom |