XYRON™ AG211
| Category: | Nylon+PPE , Polyamide + PPE |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | XYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8QRUfG_XYRON-AG211.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified PPE PA/PPE alloy 10% Filler reinforced Non-Flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(3.00 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 94.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 148 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 11 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 199 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 65°C) | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 5.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength 3(2.00 mm) | 27 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.20 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 5.0E-3 | ||
| 1 MHz | 0.010 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 120x80x3 mm |
| 2 . | 4 mm |
| 3 . | Short time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman PS 810 | Shuman Plastics, Inc. | PS (HIPS) | Shuman PS |
| Xuchuan XWB-315 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| THERMOLAST® K TC7WEZ (Series: UV/HF) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Sylvin 9604A-80 Clear 8159 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ULTEM™ 2210 resin | SABIC Innovative Plastics | PEI | ULTEM™ |