COSMOPLENE® AS164
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8PyA8Q_COSMOPLENE-AS164.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOPLENE AS164 is melt stable, high stiffness, super high impact PP copolymer manufactured by gas phase process licensed from Sumitomo Chemical Co. Japan. COSMOPLENE AS164 is suitable for products such as injection for seat bottom, extrusion for corrugated sheet, pipe and fittings, bicycle rims, blow bottle etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 1.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 2.00 mm | 1.5 | % | |
| Across Flow : 2.00 mm | 1.4 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 28.5 | MPa | |
| Break | 26.0 | MPa | |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 62 | J/m | |
| 23°C | 490 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 117 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 190 to 230 | °C | |
| Front Temperature | 190 to 230 | °C | |
| Mold Temperature | 30.0 | °C | |
| Injection Pressure | 6.86 | MPa | |
| Clamp Tonnage | 0.98 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Isocor™ CN30BT | Shakespeare Monofilaments and Specialty Polymers | Nylon 610 | Isocor™ |
| Karina IVORY PVC COMPOUND -E 809D35/ 1-CY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 6034-85 Black 299 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Hostacom TRC 352NA 95T CORNSILK | LyondellBasell Industries | TPO (POE) | Hostacom |
| SIBUR Synthetic Rubber SBR-1706 Grade C | SIBUR | SBR, Emulsion | SIBUR Synthetic Rubber |