BJB Silicone TC-5027 A/B
| Category: | Silicone , Silicone |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Silicone |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8PMxri_BJB-Silicone-TC-5027-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-5027 A/B is a brushable grade room temperature vulcanizing rubber intended primarily for making glove molds as well as parts. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A | 1.147 | g/cm³ | |
| Part B | 1.027 | g/cm³ | |
| Shrinkage | Negligible | ASTM D2566 | |
| Viscosity - Mixed (24°C) | semi-paste | cP |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Demold Time | 16.0 to 24.0 | hr | |
| Work Time 1 | 45.0 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 23 to 27 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 3.79 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Tear Strength | 17.5 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 10 | ||
| Shelf Life | 26 | wk |
| Note Message | |
|---|---|
| 1 . | 1 lbm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 9607 | Chevron Phillips Chemical Company LLC | HDPE | MarFlex® |
| Propilven B-325 | Propilven, S.A. | PP Random Copolymer | Propilven |
| KRATON® D1164 P | Kraton Polymers LLC | SIS | KRATON® |
| LUVOCOM® 1100-7721/WT9016 | Lehmann & Voss & Co. | PESU | LUVOCOM® |
| Sylvin 9302-70 White 1300 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |