LNP™ COLORCOMP™ D1000P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8OQFVv_LNPCOLORCOMPD1000Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP D1000P is a compound based on Polycarbonate resin containing Unfilled Custom Color. Added features of this material include: Exceptional Processing. Also known as: LNP* COLORCOMP* Compound D-1000 EP RD1-934 TP Product reorder name: D1000P |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.75 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.65 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2210 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 62.1 | MPa | ASTM D638 |
| Yield | 64.0 | MPa | ISO 527-2 |
| Fracture | 56.5 | MPa | ASTM D638 |
| Fracture | 59.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.3 | % | ASTM D638 |
| Yield | 5.6 | % | ISO 527-2 |
| Fracture | 79 | % | ASTM D638 |
| Fracture | 87 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Flexural Stress | 81.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 540 | J/m | ASTM D256 |
| 23°C 2 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 124 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 124 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 299 - 316 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EL-Lene™ H6105JU | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| Epoxies, Ect. 50-3150 FR | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| INNOPOL® PP CS 1-4820 MA | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| Sylvin 6930X06 Grey 9610 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 4200-55 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |