RapidCast™ RC-900
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | RapidCast™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8MhHoe_RapidCast-RC-900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RC-900 is a rigid, ABS simulated polyurethane formulated for room temperature meter-mix dispensing systems and short mold cycle times. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.08 | g/cm³ | |
| Cured | 1.12 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Compressive Modulus | 4760 | MPa | ASTM D695 |
| Compressive Strength | 75.8 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 96.0 | °C | |
| 1.8 MPa, Unannealed | 88.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 90 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 10 to 15 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.10 | Pa·s | |
| 25°C 2 | 0.43 | Pa·s | |
| 25°C 3 | 0.85 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 1.2 to 1.5 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 to 90 | ASTM D2240 | |
| Tensile Strength | 55.2 | MPa | ASTM D638 |
| Tensile Elongation at Break | 3.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ming Dih EPS S2 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Tenite™ Propionate 371A2R30012 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Tenac™-C MT754 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| 4MID® 9B20000 | 4Plas | Nylon 6 | 4MID® |
| LNP™ STAT-KON™ DEL13EXC compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |