Daelim Po1y® LH-418S
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8LePNg_Daelim-Po1y-LH-418S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daelim Po1y® LH-418S is a High Density Polyethylene product. It can be processed by injection molding and is available in Asia Pacific. Applications of Daelim Po1y® LH-418S include membranes and sheet. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.12 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F0) | > 3000 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 18.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 600 | % | ASTM D638 |
| Flexural Modulus | 686 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 120 | °C | ASTM D1525 |
| Oxidation Induction Time 2(200°C) | > 100 | min | ASTM D3895 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Al Pan |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solef® 6008 | Solvay Specialty Polymers | PVDF | Solef® |
| SuperLite® SL550800-100 (2.5mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Texalan® 7 Series 765A | Austin Novel Materials Co. Ltd. | TPU Alloy | Texalan® 7 Series |
| BJB Polyurethane WC-782 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| API II 395 | API II, Inc. | PS (GPPS) | API II |