LNP™ LUBRICOMP™ DL002P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8L0eqk_LNP-LUBRICOMP-DL002P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* DL002P is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Exceptional Processing, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DL-4020 EP Product reorder name: DL002P |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.24 | g/cm³ | ASTM D792 |
| -- | 1.25 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.70 to 0.90 | % | |
| Across Flow : 24 hr | 1.0 to 1.2 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2450 | MPa | ASTM D638 |
| -- | 2460 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 53.1 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2 |
| Break | 44.1 | MPa | ASTM D638 |
| Break | 43.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.3 | % | ASTM D638 |
| Yield | 5.6 | % | ISO 527-2 |
| Break | 31 | % | ASTM D638 |
| Break | 23 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2200 | MPa | ASTM D790 |
| -- | 2080 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 82.7 | MPa | ASTM D790 |
| -- | 85.6 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.28 | ||
| vs. Itself - Static | 0.17 | ||
| Wear Factor - Washer | 97.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 34.3 | J | ASTM D3763 |
| -- | 74.1 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 120 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 123 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.3E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vibrathane® B844 | Chemtura | PUR-Ether/TDI | Vibrathane® |
| ACRYLITE® Resist ZK-F | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |
| GERMAMID 6 GF 10 H | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| Karina BLACK PVC COMPOUND 834-48/ 1-A-ERM-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PermaStat® 1200 | RTP Company | TPU-Polyester | PermaStat® |