TUFLIN™ HS-7001 NT 7
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | TUFLIN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8KF6ui_TUFLIN-HS-7001-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TUFLIN™HS-7001 NT 7 linear low density polyethylene resin is an antioxidant modified ethylene-hexene copolymer resin used for casting extrusion. The resin is supplied in the form of pellets. The film prepared by HS-7001 NT 7 has high transparency, high tensile strength, high elongation and good puncture strength. The resin has excellent drafting properties. Main features:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 165 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 172 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 32.4 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 29.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 750 | % | ASTM D882 |
| TD : Break, 25 µm | 830 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25 µm | 370 | g | ASTM D1922 |
| TD : 25 µm | 500 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (45°, 25.4 µm) | 90 | ASTM D523 | |
| Haze (25.4 µm) | 2.5 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 266 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 可采用传统的槽型铸造薄膜挤出设备进行挤压，只需进行微小的机器改造以获得最佳使用效果。 熔体温度：510°F (265°C) |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime PP PO 500 | Primex Plastics Corporation | PP Copolymer | Prime PP |
| SWANCOR Epoxy 977 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Ad-Tech Polyester NO. 26 | Ad-Tech Plastic Systems Corp. | Polyester, TS | Ad-Tech Polyester |
| Elastocon® OF65 | Elastocon TPE Technologies | TPE | Elastocon® |
| Monprene® CP-11150 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |