Plenco 06343 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8KA00X_Plenco-06343-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 06343 is a mica reinforced phenolic molding compound, offering for a low power factor, low electrical losses, and good electrical properties after long exposures to high humidity. UL recognized under component file E40654. 06343 is available in natural color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.73 | g/cm³ | ASTM D792 |
| Apparent Density | 0.81 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.33 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 77 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 | MPa | ASTM D638 |
| Tensile Strength | 42.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.30 | % | ASTM D638 |
| Flexural Modulus | 14100 | MPa | ASTM D790 |
| Flexural Strength | 87.4 | MPa | ASTM D790 |
| Compressive Strength | 173 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 21.3 | J/m | ASTM D256 |
| Notched Izod Impact | 18 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 185 | °C | ASTM D648 |
| Continuous Use Temperature | 216 | °C | ASTM D794 |
| CLTE - Flow | 2.1E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.8E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 19 | kV/mm | ASTM D149 |
| -- 2 | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.90 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.034 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Oxygen Index | 43 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.04%Drop Ball Impact, PLENCO Method: 85 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miraprene® QS1621 | Mitsubishi Chemical Corporation | TPO (POE) | Miraprene® |
| Tecomid® NB30 BK EF | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| New-prene™ 9260N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| EMPILON® HA363 | EMPILON | SEBS | EMPILON® |
| LNP™ LUBRICOMP™ WX95752L compound | SABIC Innovative Plastics Asia Pacific | PBT | LNP™ LUBRICOMP™ |