ALCUDIA® LDPE PE-034
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8I2NQQ_ALCUDIA-LDPE-PE-034.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® PE034/A is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown or cast film applications. This material offers easy processability and good balance of mechanical and optical properties. It contains antioxidant additive and antiblock additives. TYPICAL APPLICATIONS
Recommended melt temperature range from 190-220°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 200 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 200 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 200 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Fracture, 200 µm, blown film | 21.0 | MPa | ISO 527-3 |
| TD : Fracture, 200 µm, blown film | 19.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 200 µm, blown film | 550 | % | ISO 527-3 |
| TD : Fracture, 200 µm, blown film | 650 | % | ISO 527-3 |
| Dart Drop Impact (200 µm, blown film) | 700 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 200 µm, blown film | 6.0 | N | ISO 6383-2 |
| TD : 200 µm, blown film | 9.5 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 94.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45 °, 200 µm, blown film) | 55 | ASTM D2457 | |
| Haze (200 µm, blown film) | 20 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 200 µm thickness film, blow up ratio 2.25:1, frost line height 60 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® F701-ABK-15 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| XYCOMP® 5101 | Greene, Tweed & Co. | PEEK | XYCOMP® |
| Colorite CS Series CS8039UL | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Hostacom TRC 352N E1 | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| Sylvin 29168-70 Grey 9605 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |