Kepamid® 2315GF
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Hv9O3_Kepamid-2315GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KEPAMID 2315GF is a glass fiber 15% reinforced nylon66. Mechanical and thermal property are good. It is applicable for automobile, electronic and electrical applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 115 | ASTM D785 | |
| R-Scale | 121 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Break | 125 | MPa | ISO 527-2 |
| -- | 120 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break | 2.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5300 | MPa | ASTM D790 |
| -- | 5650 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 190 | MPa | ASTM D790 |
| -- | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 245 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 260 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Hopper Temperature | 260 to 270 | °C | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Nozzle Temperature | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® 70G33HS1L BK031 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| AKROMID® A3 GF 60 natural (2424) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Aplax P2515CN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| Indothene LL 20FY010 | Reliance Industries Limited | LLDPE | Indothene LL |
| CYCOLAC™ DL100LG resin | SABIC Innovative Plastics Europe | ABS | CYCOLAC™ |