INEOS LDPE 19N430

Category:	LDPE , Low Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	INEOS LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	8HVbl1_INEOS-LDPE-19N430.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Benefits & Features
19N430 special polymer structure gives the following properties:

For extrusion coating:

Well balanced Neck In and Draw Down performance

Good adhesion performance and sealing properties

For injection moulding and compounding:

Excellent flexibility

Good transparency

Absence of any kind of additive allowing tailor formulation of specific compounds and master-batches

Applications
Extrusion coating and laminating grade designed for a medium to high coating line speed.

19N430 is also suitable for injection moulding of flexible products (caps and closures, food containers, soft tubes, technical parts) as well as for the production of compounds.

General Information
Features	Additive Free Good Adhesion Good Flexibility Homopolymer Low Density
Uses	Caps Closures Coating Applications Compounding Food Containers Laminates Masterbatch Tubing
RoHS Compliance	Contact Manufacturer
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Compounding Extrusion Coating Injection Molding Laminating

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.920	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	7.5	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 1 sec, Compression Molded)	47		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C, Injection Molded)	170	MPa	ISO 527-2/1BA/1
Tensile Stress			ISO 527-2/50
Yield, 23°C, Compression Molded	9.00	MPa
Break, 23°C, Compression Molded	10.0	MPa
Tensile Strain (Break, 23°C, Compression Molded)	550	%	ISO 527-2/50

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	87.0	°C	ISO 306/A50
Melting Temperature ¹	108	°C	ISO 11357-3

Injection	Nominal Value	Unit
Processing (Melt) Temp	190 to 250	°C

Extrusion	Nominal Value	Unit
Melt Temperature	280 to 325	°C

Note Message
1 .	DSC 2nd heating 10°C/min

Resin Grade	Manufacturer	Category	Trademark
Topolymer® 9210-551	Dongguan Top Polymer Enterprise	TPV	Topolymer®
Geon™ Vinyl Flexible R291AE	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
Polifor® L6 GF/30 NERO X2	SO.F.TER. SPA	PP Homopolymer	Polifor®
POTICON RT8	Otsuka Chemical Co., Ltd.	PPS	POTICON
3M™ Dyneon™ Fluoroelastomer FE 5530	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer