EL-Lene™ H5604F
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8GsnhR_EL-Lene-H5604F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-LENE H5604F is a product of bi-modal process from Mitsui Chemicals, Inc. of Japan. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.040 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 25% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693B |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 10 to 25 µ | ||
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 12 µm | 804 | MPa | |
| 2% Secant, TD : 12 µm | 785 | MPa | |
| Tensile Strength | ASTM D882 | ||
| TD : Yield, 12 µm | 24.5 | MPa | |
| MD : Break, 12 µm | 60.8 | MPa | |
| TD : Break, 12 µm | 30.4 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 12 µm | 240 | % | |
| TD : Break, 12 µm | 450 | % | |
| Dart Drop Impact (12 µm) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 12 µm | 3.0 | g | |
| TD : 12 µm | 80 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Melting Temperature | 131 | °C | ASTM D2117 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen P 9421 66408 | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® Vestolen P |
| Spartech Polycom SCR21-1091 | Spartech Polycom | PBT | Spartech |
| WPP PE PE25-Black | Washington Penn Plastic Co. Inc. | MDPE | WPP PE |
| Osterlene® PPH-3.5-LWC | Osterman & Company | PP Homopolymer | Osterlene® |
| POFEX 8200EP80F | POLYROCKS CHEMICAL CO., LTD | TPE | POFEX |