Braskem PE SEB853
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem America Inc. |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Gqczl_Braskem-PE-SEB853.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: SEB853 is a low density polyethylene produced under high pressure technology. Films obtained with this product show outstanding optical properties, good sealability, and low gel content. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Applications: Typical blown film applications include films for diapers and other general purposes as well as LLDPE and HDPE blends. Process: Blown and Cast Film Extrusion |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.7 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 40.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 300 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 280 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm, Blown Film) | 50 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (38 µm, Blown Film) | 100 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60 °, blown film) | 113 | ASTM D2457 | |
| Haze (Blown Film) | 5.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 95 | % | ASTM D6866 |
| Blown Film Properties: Obtained in 75mm extruder, blow up ratio 2:1, die gap 1.0mm and 38µm thickness.Recommended process conditions:Blown Film ExtrusionExtruder:Screw- relation L/D..........16 to 30:1Compression Ratio.........3 to 4:1Screw Package (Mesh)...40/60/40Temperature Profile: 1st zone............................110°C Extruder..........................150°C Die..................................160°C Blow up ratio...................from 2 to 3:1Frostline Height...............maximum equivalent to bubble diameter |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zetpol® 4310 | Zeon Corporation | NBR | Zetpol® |
| AKROMID® B3 GF 15 1 L black (4670) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Gallonprene® GP420-9002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Lupoy® SC1004AU | LG Chem Ltd. | PC | Lupoy® |
| RTP 799 X 143519 EG | RTP Company | HDPE | RTP |