Sinkral® F 332
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Sinkral® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8GmXg9_Sinkral-F-332.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sinkral F 332 is a general purpose injection moulding grade which combines excellent thermal stability during processing with a good balance between flow and impact characteristics. Designation: Thermoplastic ISO 2580-ABS 1,MGN,105-15-16-20 Suitable for use in a variety of industrial sectors, for the production of small household appliances and white goods, vacuum cleaners and telephones. Grade available in natural colour only. The composition of this grade, on request, can meet European Regulations for packaging in contact with foodstuff. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 42.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 60 | % | ASTM D638 |
| Flexural Modulus 3 | 2250 | MPa | ASTM D790 |
| Flexural Strength 4 | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | DIN 53453 |
| Charpy Unnotched Impact Strength | DIN 53453 | ||
| -40°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -40°C, 3.20 mm | 90 | J/m | ISO 180/4A |
| -20°C, 3.20 mm | 100 | J/m | ISO 180/4A |
| 0°C, 3.20 mm | 130 | J/m | ISO 180/4A |
| 23°C, 3.20 mm | 190 | J/m | ISO 180/4A |
| -40°C 5 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 6 | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 101 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 107 | °C | ISO 306/A120 |
| -- | 102 | °C | ISO 306/B120 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 kHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (1 kHz) | 0.015 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (3.00 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastic ISO 2580-ABS 1,MGN,105-15-16-20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 4 mm |
| 6 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® NY1599-GY | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| WPP PP PPC3GF1.5UV-MS 428 Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Zetpol® 3310EP | Zeon Chemicals L.P. | NBR | Zetpol® |
| DOMAMID® 6AF IE | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Ecodear® Prototype - High Flow | Toray Resin Company | PLA | Ecodear® |