DENYL 66 3010
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | DENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8GSuDY_DENYL-66-3010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 30% glass fiber reinforced, not Flame Retardant compound, very good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.50 | -- | % | |
| Across Flow | 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | -- | MPa | ASTM D638 |
| Tensile Strength | ||||
| Yield | 180 | 130 | MPa | ASTM D638 |
| Yield | -- | 130 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | -- | % | ASTM D638 |
| Flexural Modulus | -- | 6100 | MPa | ASTM D790, ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 10 | -- | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 70 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | -- | °C | ASTM D648A |
| Vicat Softening Temperature | 250 | -- | °C | ASTM D1525 1 |
| RTI Elec | 140 | -- | °C | UL 746 |
| RTI Imp | 140 | -- | °C | UL 746 |
| RTI Str | 140 | -- | °C | UL 746 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 100 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer P-11030-CT | Polylink Polymers (India) Ltd. | TPO | Polylink Polymer |
| Tarnamid® T- 27 GF35 P5 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Tisoplen® PPH 30 GFR | Tisan | PP Homopolymer | Tisoplen® |
| Next Nylon 6 Prime Series NM15-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| SABIC® PPcompound 8533 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |