LNP™ THERMOCOMP™ RF006H compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8G1IOt_LNP-THERMOCOMP-RF006H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* RF006H is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare. Also known as: LNP* THERMOCOMP* Compound RF-1006 Product reorder name: RF006H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.40 1.41 | g/cm³ | ASTM D792 |
| -- | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 1.4 to 1.6 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.69 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8980 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 1 | 165 | MPa | ASTM D638 |
| Break | 154 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 2 | 2.4 | % | ASTM D638 |
| Break | 2.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 3 | 9440 | MPa | ASTM D790 |
| -- 4 | 9220 | MPa | ISO 178 |
| Flexural Strength 5(Break, 50.0 mm Span) | 235 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.71 | ||
| vs. Itself - Static | 0.57 | ||
| Wear Factor - Washer | 75.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 6 | 7.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 650 | J/m | ASTM D4812 |
| 23°C 7 | 52 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.50 | J | ASTM D3763 |
| -- | 2.57 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 265 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 255 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 8 | 243 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.3E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tygon R-3400 | Saint Gobain - Norton | PVC, Unspecified | Tygon |
| CERTENE™ HPB-0360 | Muehlstein | HDPE | CERTENE™ |
| Cogegum® GFR/340-HP | Solvay Specialty Polymers | Polyolefin, Unspecified | Cogegum® |
| Daelim Po1y® VL0001EN | DAELIM INDUSTRIAL CO., LTD. | Plastomer | Daelim Po1y® |
| LNP™ LUBRICOMP™ KL002 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |