ULTEM™ STM1500 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8FWHFs_ULTEM-STM1500-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Siloxane polyetherimide block copolymer. Wire and cable use. Strength and flexibility. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (295°C/6.6 kg) | 12 | g/10 min | ASTM D1238 |
| Water Absorption 1(Equilibrium) | < 0.25 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 28.3 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 100 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 386 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 26.0 | mg | ASTM D1044 |
| Elongation at Break | UL 1561 | ||
| -- 5 | 400 | % | |
| Aged 1 week : 135°C | 370 | % | |
| Retention 1 week : 135°C | 94 | % | |
| Tensile Strength at Break | UL 1561 | ||
| -- 6 | 37.9 | MPa | |
| Aged 1 week : 135°C | 38.6 | MPa | |
| Retention 1 week : 135°C | 100 | % |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | 0 | Internal Method | |
| OSU Peak Heat Release Rate 7 | 140 | kW/m² | FAR 25.853 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cable Wall Thickness | 254.0 | µm | Internal Method |
| Corrosion | ASTM E5.2170 | ||
| 1 hr 8 | 4.00 | nm | |
| 24 hr | 12.2 | nm | |
| 6 days | 18.3 | nm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 168 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 4.1E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| 3.20 mm, in Air | 16 | kV/mm | |
| 3.20 mm, in Oil | 16 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.01 | ||
| 60 Hz | 3.01 | ||
| 100 kHz | 2.79 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 0.010 | ||
| 60 Hz | 0.010 | ||
| 100 kHz | 5.6E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 46 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 293 to 316 | °C | |
| Front Temperature | 293 to 316 | °C | |
| Nozzle Temperature | 299 to 321 | °C | |
| Processing (Melt) Temp | 299 to 321 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Estimated |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | Cable Wall Thickness 10 mil |
| 6 . | Cable Wall Thickness 10 mil |
| 7 . | 5 minute test |
| 8 . | 2500 angstroms max |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinelec CCB1844 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinelec |
| Sinpolene MBB3401 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| SureSpec PET-80S | Genesis Polymers | PET | SureSpec |
| AKROMID® A3 GF 40 1 black (2386) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| DIOSHY® TPU T998M | DIOSHY Co.,Ltd. | TPU-Polyester | DIOSHY® |