SABIC® HDPE M453G
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Bh14N_SABICHDPEM453G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE M453G exhibits a good impact resistance, even at low temperatures. Typical applications are Caps & closures, Crates & boxes and PE-Xb pipes for hot and cold water and central floor heating. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 4.7 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 13 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (40°C, 1.00mm, 10% Igepal CO-630, compression molding) | 60.0 | hr | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1BA/50 | ||
| 2.00, molded | 1100 | MPa | ISO 527-2/1BA/50 |
| 1% Secant : mm, molded | 1200 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 26.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 25.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 200 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 26.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 4.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 81.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 124 | °C | ISO 306/A |
| Melting Temperature (DSC) | 132 | °C | ISO 11357-3 |
| Enthalpy Change | 203 | J/g | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1280 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| PrimoPrene 70A-4000 | KMI Group Inc. | TPV Alloy | PrimoPrene |
| DIAMALOY ABSPC 9902 LM 1402 Black | Network Polymers, Inc. | PC+ABS | DIAMALOY ABSPC |
| Softell TKG 317N C12740 | LyondellBasell Industries | PP Copolymer | Softell |
| LubriOne™ PC-000/05T Split Brown Black | PolyOne Corporation | PC | LubriOne™ |