SABIC® PPcompound 7985
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Bb7HG_SABIC-PPcompound-7985.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 7985 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with interior automotive UV stability. The IMDS is 209747565. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.02 | g/cm³ | ASTM D792 |
| -- | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 80°C, 1 hr | 1.4 | % | |
| Across Flow : 23°C, 48 hr | 1.2 | % | |
| Flow : 80°C, 1 hr | 1.0 | % | |
| Flow : 23°C, 48 hr | 0.80 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2780 | MPa | ASTM D638 |
| -- | 2190 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 27.0 | MPa | ASTM D638 |
| Yield | 27.0 | MPa | ISO 527-2/50 |
| Break 3 | 20.0 | MPa | ASTM D638 |
| Break | 20.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 22 | % | ASTM D638 |
| Break | 14 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1940 | MPa | ASTM D790 |
| 64.0 mm Span 7 | 2220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 8 | 2.4 | kJ/m² | |
| 0°C 9 | 2.5 | kJ/m² | |
| 23°C 10 | 6.5 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm 11 | 45 | J/m | ASTM D256 |
| -30°C 12 | 2.2 | kJ/m² | ISO 180/1A |
| 0°C 13 | 2.8 | kJ/m² | ISO 180/1A |
| 23°C 14 | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact 15(23°C, 3.20 mm) | 1100 | J/m | ASTM D4812 |
| Instrumented Dart Impact 16 | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 2.60 | J | |
| 0°C, Energy at Peak Load | 7.60 | J | |
| 23°C, Energy at Peak Load | 22.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 114 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 17 | 108 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 18 | 61.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 144 | °C | ISO 306/A50 |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 7.50 | µm/Mk | |
| Transverse : -30 to 100°C | 18.0 | µm/Mk |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4mm, Cut |
| 9 . | 80*10*4 mm, Cut |
| 10 . | 80*10*4 mm, Cut |
| 11 . | 63.5*12.7*3.2mm, Cut |
| 12 . | 80*10*4mm, Cut |
| 13 . | 80*10*4mm, Cut |
| 14 . | 80*10*4mm, Cut |
| 15 . | 63.5*12.7*3.2mm, Cut |
| 16 . | 6.60 m/sec |
| 17 . | 80*10*4mm, Cut |
| 18 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Eltex® MED 200-MG02 | INEOS Olefins & Polymers Europe | PP Random Copolymer | Eltex® MED |
| KumhoSunny ABS 740 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| KEBAFORM® C 3090(K) | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| LNP™ THERMOCOMP™ DC0041PQ compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| SQUARE® LIM8620-70A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |