OnFlex™ BIO 5370A-E0004
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnFlex™ BIO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8BOgCg_OnFlex-BIO-5370A-E0004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| OnFlex™-Bio 5300 series thermoplastic elastomer polymers are thermoplastic polyurethane compounds produced from renewable natural resources. According to ASTM-D6866 certification, these compounds contain at least more than 20% renewable materials. OnFlex™-Bio 5300 series compounds have good surface finish, soft hand feeling, wear resistance and mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 63.0 | mm³ | DIN 53516 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Odor rating 1 | 3.0 | VDA 270 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2 | DIN 53504 | ||
| Lateral flow : 100% strain, 23°C, 2.00mm | 3.30 | MPa | DIN 53504 |
| Traffic : 100% strain, 23°C, 2.00mm | 3.80 | MPa | DIN 53504 |
| Lateral flow : 300% strain, 23°C, 2.00mm | 7.90 | MPa | DIN 53504 |
| Traffic : 300% strain, 23°C, 2.00mm | 9.20 | MPa | DIN 53504 |
| Tensile Stress 3 | DIN 53504 | ||
| Lateral flow : fracture, 23°C, 2.00mm | 11.0 | MPa | DIN 53504 |
| Traffic : fracture, 23°C, 2.00mm | 12.7 | MPa | DIN 53504 |
| Tensile Elongation 4 | DIN 53504 | ||
| Lateral flow : fracture, 23°C, 2.00mm | 410 | % | DIN 53504 |
| Traffic : fracture, 23°C, 2.00mm | 410 | % | DIN 53504 |
| Tear Strength 5 | ISO 34-1 | ||
| Lateral flow : 23°C, 2.00mm | 43 | kN/m | ISO 34-1 |
| Traffic : 23°C, 2.00mm | 47 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 51 | % | ISO 815 |
| 70°C, 22 hr | 73 | % | ISO 815 |
| 100°C, 22 hr | 84 | % | ISO 815 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| 各项属性值是采用注射模制基板测量得出。 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Method A3 |
| 2 . | Type 1, 200mm/min |
| 3 . | Type 1, 200mm/min |
| 4 . | Type 1, 200mm/min |
| 5 . | Method A, Pant-Shaped Specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2201H0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Starex GR-4015A | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Wondel® P PG8 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| BMC 400 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Sylvin 8925-70 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |