Message
Baydur 660 IBS is a black-pigmented, rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system incorporates a specially engineered interactive blowing system (IBS) and is supplied as two reactive liquid components. Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Compo- nent B is a formulated polyol system containing no CFC- or HCFC-blowing additives. Note: Component B should be agitated thoroughly prior to delivery of contents of the drum to the day tank due to possible pigment settling. The Baydur 660 IBS system was designed for general-purpose applications and is used in industrial and recreational markets. The applications typically take advantage of the material's strength, excellent surface finish, and large part capability. As with any product, use of the Baydur 660 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.

General Information
Features	Good strength General Excellent appearance
Uses	Structural Foam Industrial application General
Appearance	Black
Processing Method	Reaction Injection Molding (RIM)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.319	g/cm³	ASTM D792
Molding Shrinkage - Flow (6.35 mm)	0.30 - 0.50	%	ASTM D955

Hardness	Nominal Value	Test Method
Durometer Hardness		ASTM D2240
Shaw D, 6.35mm	37	ASTM D2240
Shaw D, 12.7mm	39	ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Fracture, 6.35mm	6.07	MPa	ASTM D638
Fracture, 12.7mm	6.21	MPa	ASTM D638
Tensile Elongation			ASTM D638
Fracture, 6.35mm	7.0	%	ASTM D638
Fracture, 12.7mm	9.0	%	ASTM D638
Flexural Modulus			ASTM D790
6.35 mm	303	MPa	ASTM D790
12.7 mm	248	MPa	ASTM D790
Flexural Strength			ASTM D790
6.35 mm	8.27	MPa	ASTM D790
12.7 mm	8.96	MPa	ASTM D790
Compressive Strength			ASTM D695
6.35 mm	6.07	MPa	ASTM D695
12.7 mm	3.79	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength ¹	5.3	kJ/m²	Internal method

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, unannealed, 6.35mm	77.0	°C	ASTM D648
0.45 MPa, unannealed, 12.7mm	96.0	°C	ASTM D648

Thermoset	Nominal Value
Thermoset Components
Component a	Mixing ratio by weight: 120
Component B	Mixing ratio by weight: 100

Additional Information
Part A Type: Isocyanate Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 cps Flash Point PMCC: 199°C NCO: 31.0 min wt% Part B Type: Polyol Appearance: Black liquid Specific Gravity @ 25°C: 1.05 Viscosity @25°C: 2000 cps Flash Point PMCC: 131°C Water: 0.64 wt% Material Temperatures: 32 to 35°CMold Temperature: 55 to 66°CHand Mix Reactivity at 25°C Cream Time: 22 to 34 sec Gel Time: 46 to 58 sec Tack Free Time: 58 to 80 sec Free-Rise Density: 7.5 to 9.0 lb/ft³ Polyol Nucleation Specific Gravity: 0.85 to 0.95 0Recommended Shot Time: 5 to 6 sec

Additional Information

Part A Type: Isocyanate Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 cps Flash Point PMCC: 199°C NCO: 31.0 min wt% Part B Type: Polyol Appearance: Black liquid Specific Gravity @ 25°C: 1.05 Viscosity @25°C: 2000 cps Flash Point PMCC: 131°C Water: 0.64 wt% Material Temperatures: 32 to 35°CMold Temperature: 55 to 66°CHand Mix Reactivity at 25°C Cream Time: 22 to 34 sec Gel Time: 46 to 58 sec Tack Free Time: 58 to 80 sec Free-Rise Density: 7.5 to 9.0 lb/ft³ Polyol Nucleation Specific Gravity: 0.85 to 0.95 0Recommended Shot Time: 5 to 6 sec

Note Message
1 .	0.5

Category:	PUR-MDI , Polyurethane (MDI)
Manufacturer:	Covestro - PUR
Trademark:	Baydur®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	89k3CX_Baydur-660-IBS-30-pcf-.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Shanghai Potomer SG8	Shanghai Potomer International Trade Co., Ltd.	PVC, Rigid	Shanghai Potomer
Dynacom 101-G20	Dynachem Co. Ltd.	PBT	Dynacom
ESTACARB PC 0860GF V1	Cossa Polimeri S.r.l.	PC	ESTACARB
LNP™ LUBRICOMP™ IFL21 compound	SABIC Innovative Plastics	Nylon 612	LNP™ LUBRICOMP™
PolyFibra® PF-PEF04	FuturaMat	PP, Unspecified	PolyFibra®