Zhongfa PC G2830
| Category: | PC , Polycarbonate |
| Manufacturer: | Yuyao Zhongfa Engineering Plastics Co. Ltd. |
| Trademark: | Zhongfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 88k3cB_Zhongfa-PC-G2830.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Zhongfa PC G2830 is a polycarbonate (PC) material, which contains a 30% glass fiber reinforced material. This product is available in the Asia-Pacific region and is processed by injection molding. The main features of Zhongfa PC G2830 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 130 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 7000 | MPa | ASTM D790 |
| Flexural Strength | 175 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 151 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 147 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-1 | UL 94 | |
| 3.20 mm | V-1 | UL 94 |
| Additional Information |
|---|
| Flexural Modulus, ASTM D790: 6000 to 8000 MPaFlexural Strength, ASTM D790: 155 to 195 MPaHDT at 264 psi, ASTM D648: 146 to 148°CHDT at 66 psi, ASTM D648: 150 to 152°CNotched Izod Impact, ASTM D256: 12 to 18 kJ/m²Tensile Elongation, ASTM D638: 4 to 6%Tensile Strength, ASTM D638: 125 to 145 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Processing (Melt) Temp | 210 - 255 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 70.0 - 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-289 | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| ASI POLYPROPYLENE 1407H-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Infino XK-2307 | SAMSUNG SDI CO., LTD. | PPS | Infino |
| LGH 305 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGH |
| Kanghui KH2090 | Yingkou Kanghui Petrochemical Co., LTD. | PBT | Kanghui |