Dragon Skin® silicones are high performance platinum cure liquid silicone compounds that are used for a variety of applications ranging from creating skin effects and other movie special effects to making production molds for casting a variety of materials. Because of the superior physical properties and flexibility of Dragon Skin® rubbers, they are also used for medical prosthetics and cushioning applications. Dragon Skin® rubbers are also used for a variety of industrial applications and have a service temperature range of a constant -70°F to +400°F (-21°C to + 205°C). Great for Making Molds for a Variety of Applications - Available in Shore 10A, 20A and 30A, Dragon Skin® silicones can be used to make exceptionally strong and tear resistant molds for casting plaster, wax, concrete, resins and other materials. Time Tested, Versatile Special Effects Material - Soft, super-strong and stretchy, Dragon Skin® 10 (Fast, Medium and Slow speeds) is used around the world to make spectacular skin and creature effects. An infinite number of color effects can be achieved by adding Silc Pig® silicone pigments or Cast Magic® effects powders. Cured rubber can also be painted with the Psycho Paint® system. Easy To Use - Dragon Skin® silicones are mixed 1A:1B by weight or volume. Liquid rubber can be thinned with Silicone Thinner® or thickened with THI-VEX® II. Rubber cures at room temperature (73°F/23°C) with negligible shrinkage. Vacuum degassing is recommended to minimize air bubbles in cured rubber. |
General Information | |
---|---|
Features |
|
Uses |
|
Appearance |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.07 | g/cm³ | ASTM D1475 |
Specific Volume | 0.932 | cm³/g | ASTM D1475 |
Additional Information | Nominal Value | Unit | Test Method |
---|---|---|---|
Mixing Ratio | 1A:1B by volume or weight | ||
Operating Temperature | -54 to 232 | °C |
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Molding Shrinkage - Flow | < 0.10 | % | ASTM D2566 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Durometer Hardness (Shore A) | 10 | ASTM D2240 |
Elastomers | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress (100% Strain) | 0.152 | MPa | ASTM D412 |
Tensile Strength (Break) | 3.28 | MPa | ASTM D412 |
Tensile Elongation (Break) | 1000 | % | ASTM D412 |
Tear Strength 1 | 17.9 | kN/m | ASTM D624 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Dielectric Strength | > 14 | kV/mm | ASTM D149 |
Thermoset | Nominal Value | Unit | Test Method |
---|---|---|---|
Pot Life | 8.0 | min | ASTM D2471 |
Thermoset Mix Viscosity | 23000 | cP | ASTM D2393 |
Demold Time | 75 | min |
Note Message | |
---|---|
1 . | Die B |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Riteflex® 655HS | Celanese Corporation | TPC-ET | Riteflex® |
HiFill® PA6 GF10 L BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
LACTEL® 65:35 DL-PLG | DURECT Corporation | PLA | LACTEL® |
Innothane® IE-60DC | Innovative Polymers, Inc. | TSU | Innothane® |
TPX® RT31 | Mitsui Chemicals, Inc. | PMP Copolymer | TPX® |