BJB Polyurethane TC-962 A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 86vmfg_BJB-Polyurethane-TC-962-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
TC-962 A/B is a multi-purpose elastomer that can perform many functions. Typical product uses are:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ASTM D792 |
| Viscosity- Mixed (cps) (25°C) | Semi-paste | ASTM D2393 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Work Time 1(25°C) | 15.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time | 5.0 - 7.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 58 - 62 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 5.86 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 450 | % | ASTM D412 |
| Tear Strength | 31.5 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Shelf Life | 26 | wk | |
| Demold Time (25°C) | 480 - 840 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 160°F (71°C). |
| Note Message | |
|---|---|
| 1 . | 100g mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® K190-BTT-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| YUNGSOX® PP 5350T | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| Ultramid® A3EG6 BK00564 | BASF Corporation | Nylon 66 | Ultramid® |
| Chemraz 505 | Greene, Tweed & Co. | PTFE | Chemraz |
| ESENTTIA 01R25 | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |