Edgetek™ PK-30GF/000 FCR NC
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 86RHER_Edgetek-PK-30GF-000-FCR-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30 % Glass Fiber Reinforced PEEK Compound with Ultra High Flowability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage (3.00 mm) | 0.20 - 0.50 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 190 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 - 4.0 | % | ASTM D638 |
| Flexural Modulus 2 | 11000 | MPa | ASTM D790 |
| Flexural Strength 3 | 290 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | 950 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 320 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 160 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 350 - 390 | °C | |
| Middle Temperature | 350 - 390 | °C | |
| Front Temperature | 350 - 390 | °C | |
| Mold Temperature | 170 - 190 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 30 FR2 A LM WEISS 96.0342 LM | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Witcom PEI 3L1 | Witcom Engineering Plastics B.V. | PEI | Witcom PEI |
| GLS PP YN06 MH1 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| Kingfa APO-3012 | Kingfa | PP, Unspecified | Kingfa |
| Polimid A 25 GF V0A TR1 | Poliblend S.p.a. | Nylon 66 | Polimid A |