PALDUR®R 20 is a polybutene terephthalate (PBT) product,. It can be processed by injection molding and is available in Europe. PALDUR®R 20 applications include electrical/electronic applications, wire and cable, housing and automotive industries. Features include: flame retardant/rated flame high viscosity Rapid Prototyping Cycle chemical resistance

General Information
Features	Fast molding cycle Good chemical resistance Viscosity, High
Uses	Electrical/Electronic Applications Application in Automobile Field Communication Equipment Shell
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.30	g/cm³	ISO 1183
Water Absorption			ISO 62
Saturated, 23°C	0.45	%	ISO 62
Equilibrium, 23°C, 50% RH	0.18	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2450	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	52.5	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	4.0	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	50	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.5	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	186	°C	ISO 306/B50
Melting Temperature (DSC)	225	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2300 to 2600 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 50 to 55 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 3 to 5 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 3 to 4 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 177 to 180 °CDensity, ISO 1183: 1.29 to 1.31 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.4 to 0.5 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2300 to 2600 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 50 to 55 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 3 to 5 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 3 to 4 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 177 to 180 °CDensity, ISO 1183: 1.29 to 1.31 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.4 to 0.5 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Resin Grade	Manufacturer	Category	Trademark
PRIMALENE WPP852	Southern Polymer, Inc.	HDPE, HMW	PRIMALENE
Sindustris PC GP1001M	Sincerity Australia Pty Ltd.	PC	Sindustris PC
Softell TKG 259N	LyondellBasell Industries	Polyolefin, Unspecified	Softell
4MID® 9A32335 I	4Plas	Nylon 66	4MID®
LEXAN™ HFD1212 resin	SABIC Innovative Plastics	PC	LEXAN™

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	pal plast GmbH
Trademark:	PALDUR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	836Myc_PALDUR-R-20.pdf
PRICE:	Order Products email sales@su-jiao.com