Di-Pak™ E-4671
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 82ofP4_Di-Pak-E-4671.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DI-PAK E-4600 SERIES Flexible, high strength, 50 to 71 shore D hardness potting and encapsulating systems. Available in flame retardant (FR), 3 minute (-3) gel time, and in black or unpigmented. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D2566 |
| Weight - per cubic inch | 17 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 150 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 18.0 | min | ASTM D2971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Shock Test | Pass |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 to 73 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 376 | MPa | ASTM D638 |
| Tensile Strength | 32.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 87 | % | ASTM D638 |
| Flexural Modulus | 393 | MPa | ASTM D790 |
| Flexural Strength | 25.6 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 116 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.22 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.2E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | > 14 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 1.90 | ||
| 100 kHz | 2.30 | ||
| Dissipation Factor (25°C, 100 kHz) | 0.038 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 65, Mix Ratio by Volume: 60 | ||
| Thermoset Mix Viscosity (25°C) | 2000 | cP | ASTM D4878 |
| Demold Time (21°C) | 60 to 120 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Addisil™ 472 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Bayblend® FR3050 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Bergamid™ A700 G30 H (f1) | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Huafon JF-P-8985 / JF-I-5218 | Huafon Group Co., Ltd. | PUR-Ether | Huafon |
| ULTEM™ 1000E resin | SABIC Innovative Plastics | PEI | ULTEM™ |