Hifax CB242
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8283w8_Hifax-CB242.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hifax CB242 medium melt flow, 950 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has an excellent combination of stiffness, low temperature impact resistance, processability and paintability. It was originally designed for use in automotive bumper fascia applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2 |
| Flexural Modulus | 950 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 5.3 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 81.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 51.0 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 100°C) | 6.9E-5 | cm/cm/°C | ASTM E228, ISO 11359-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Titalon® 2320 | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| Hylon® N1015THL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Lifoflex® UV 70 GA 1070 | ELASTO | SEBS | Lifoflex® |
| Lupoy® SC3154 | LG Chem Ltd. | PC | Lupoy® |
| MAXAMID™ PA66G43-NC010 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |