Plenco 04599 (Compression)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 81DS8o_Plenco-04599-Compression-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 04599 is a mineral filled, phenolic molding compound offering excellent heat resistance and dimensional stability, typically required for automotive ashtray applications. 04599 is formulated to provide improved cosmetic characteristics and mechanical strength properties. 04599 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Apparent Density | 0.62 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.38 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.21 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 89 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10100 | MPa | ASTM D638 |
| Tensile Strength | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.70 | % | ASTM D638 |
| Flexural Modulus | 9430 | MPa | ASTM D790 |
| Flexural Strength | 83.1 | MPa | ASTM D790 |
| Compressive Strength | 216 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 19.5 | J/m | ASTM D256 |
| Notched Izod Impact | 17 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| Continuous Use Temperature | 217 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.4E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 13 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.077 | ASTM D150 | |
| Arc Resistance | 159 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Additional Information |
|---|
| The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.18%Drop Ball Impact, PLENCO Method: 85 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 0.50 | hr | |
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Mold Close Time: 3-8 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BJB Polyurethane TC-891 FR REV 1 | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| APEX® RE 9015A | Teknor Apex Company | PVC, Rigid | APEX® |
| Fainplast PVC FK 90 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Plasmer 5040DN/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| 3M™ Dyneon™ PTFE Compound FB 01N | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |