Iupilon® MB6001UR
| Category: | PC+Acrylic , Polycarbonate + Acrylic (PMMA) |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 80ozZe_Iupilon-MB6001UR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Iupilon® MB6001UR is a Polycarbonate + Acrylic (PMMA) (PC+Acrylic) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Iupilon® MB6001UR: Wear Resistant. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 49 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 47.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Water Absorption (Saturation, 23°C) | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.8 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 60 | % | ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Stress | 113 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 117 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 104 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 6.1E-5 | cm/cm/°C | |
| Transverse | 6.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 285 | °C | |
| Nozzle Temperature | 270 to 285 | °C | |
| Mold Temperature | 60.0 to 95.0 | °C | |
| Injection Pressure | 50.0 to 100 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP PA66 HI 40 GF BLK | RTP Company | Nylon 66 | RTP |
| Network Polymers PP PPH 30 2000 TF40 | Network Polymers, Inc. | PP Homopolymer | Network Polymers PP |
| Bergadur™ PB40 G10 NC007 | PolyOne Corporation | PBT | Bergadur™ |
| Huafon JF-HSY-9820 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| TECACOMP® PA66 GF30 TF15 HI black 3366 | Ensinger GmbH | Nylon 66 | TECACOMP® |