Halene H M6007L
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 80LV55_Halene-H-M6007L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
M6007L is a Narrow Molecular Weight Distribution HDPE produced by Spherilene Technology. M6007L is ideally suited for injection molding of heavy-duty crates & industrial products. The precise control of morphology & MWD during polymerization confers superior processability and improved performance properties compared to conventional HDPE grades. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238 |
| Spiral Flow 2 | 43.0 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 3(Yield, Injection Molded) | 24.0 | MPa | ASTM D638 |
| Tensile Elongation 4(Break, Injection Molded) | > 500 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 850 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 50 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 132 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 185 to 235 | °C | |
| Middle Temperature | 185 to 235 | °C | |
| Front Temperature | 185 to 235 | °C | |
| Nozzle Temperature | 235 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | Melt Temperature: 235°C |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITREX® Rg-30 | Nytef Plastics, Ltd. | PEEK | UNITREX® |
| EXCELLEN® GMH GH030 | Sumitomo Chemical Asia | PE, Unspecified | EXCELLEN® GMH |
| Formolene® 2315N | Formosa Plastics Corporation, U.S.A. | PP Copolymer | Formolene® |
| Halene P M365 | Haldia Petrochemicals Ltd. | PP Impact Copolymer | Halene P |
| Karina WHITE PVC COMPOUND 806-10/ 42-B-RT-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |