Maxxam™ MX5200-5006 RS NATURAL
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7xQYCM_Maxxam-MX5200-5006-RS-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.6 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 1.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2520 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 67.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 19 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 185 to 200 | °C | |
| Middle Temperature | 200 to 215 | °C | |
| Front Temperature | 205 to 220 | °C | |
| Nozzle Temperature | 205 to 220 | °C | |
| Mold Temperature | 40.0 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 8.00 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T40P250-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| DINAPLEN® PPH1S04 G20 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| ELASTOSIL® LR 3844/40 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Infino NH-1250 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |
| LNP™ LUBRICOMP™ QAP22S compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |