LUVOCOM® 50-9310 Datasheet,PC,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®50-9310 is a polycarbonate (PC) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 50-9310 are: Flame Retardant Conductivity Good dimensional stability Good stiffness Heat resistance Typical application areas include: Electrical/electronic applications engineering/industrial accessories Automotive Industry business/office supplies medical/health care

General Information
Features	Good dimensional stability Rigid, good Static conduction Antistatic property Good liquidity Good strength Heat resistance, high Flame retardancy
Uses	Electrical/Electronic Applications Engineering accessories Application in Automobile Field Business equipment Medical/nursing supplies
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.17	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (330°C/2.16 kg)	30.0	cm³/10min	ISO 1133
Molding Shrinkage	0.80 - 1.1	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.15	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2600	MPa	ISO 527-2
Tensile Stress (Break)	75.0	MPa	ISO 527-2
Tensile Strain (Yield)	6.0	%	ISO 527-2
Flexural Modulus	2400	MPa	ISO 178
Flexural Stress	100	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	180	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	155	°C	ISO 75-2/A
Continuous Use Temperature	150	°C	UL 746B
Maximum operating temperature- Short Term	170	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	1.0E+9 - 1.0E+12	ohms	IEC 60167

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	180	°C	ISO 306/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+13	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	130	°C
Drying Time - Desiccant Dryer	2.0 - 4.0	hr
Rear Temperature	310 - 330	°C
Middle Temperature	320 - 340	°C
Front Temperature	330 - 350	°C
Nozzle Temperature	320 - 340	°C
Processing (Melt) Temp	330	°C
Mold Temperature	80 - 140	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	PC , Polycarbonate
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7wGQZ5_LUVOCOM509310.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
MIDILENA I XCF-0.3	ROMPETROL PETROCHEMICALS S.R.L.	LDPE	MIDILENA I
Unichem 8030 BLACK-HG	Colorite Polymers	PVC, Flexible	Unichem
NILAMID® B3 W M30	Nilit Plastics	Nylon 6	NILAMID®
ACRYLITE® 8N	Evonik Cyro LLC	Acrylic (PMMA)	ACRYLITE®
TECHNYL® A 218HP V30 BLACK 21N	Solvay Engineering Plastics	Nylon 66	TECHNYL®