Prime Tuff-X 500

Category:	Unspecified , Unspecified
Manufacturer:	Primex Plastics Corporation
Trademark:	Prime Tuff-X
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	7vzdeD_Prime-Tuff-X-500.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Prime Super Tuff-X 500 is an engineered alloy that offers very high stiffness when rigidity is important. Prime Super Tuff-X 500 has a very low C.L.T.E., excellent cold temperature impact, UV protection, improved rigidity and is highly chemical resistant. Applications: Ideal for : marine, automotive, power tools, electronics, lawn and garden and RV applications. Processing: Prime Super Tuff-X 500 is a semi-crystalline material that behaves differently in the thermoforming process when compared to an amorphous material. Ideal forming conditions; Mold temp. 170-190°F, Sheet temp. 320-360°F, part removal temp.145-170°F. Aluminum temperature controlled grit blasted tools are preferred. Ceramic tools can also work well if they are glass bead blasted. Quartz or ceramic heaters are preferred when working with Super Tuff-X 500. Calrod heaters can sometimes be used but gas fired is not recommended. Finishing: Super Tuff-X 500 can be fabricated by using many techniques such as; drilling, routing, punching, sawing, laser or die cut. Mechanical screws and other types of fasteners may be used to join Super Tuff-X 500 parts together. It may also be bonded with certain types of adhesives. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Our Super Tuff-X 500 material will accept any color. This product can also be painted with a two-part paint system. Super Tuff-X 500 is offered in gauges from .090 to .400 in. and in widths up to 120". Super Tuff-X 500 is offered in several different patterns that include; FL/HC, H/C, Diamond Plate, Smooth and Levant II.

Message

Prime Super Tuff-X 500 is an engineered alloy that offers very high stiffness when rigidity is important. Prime Super Tuff-X 500 has a very low C.L.T.E., excellent cold temperature impact, UV protection, improved rigidity and is highly chemical resistant.

Applications:
Ideal for : marine, automotive, power tools, electronics, lawn and garden and RV applications.

Processing:
Prime Super Tuff-X 500 is a semi-crystalline material that behaves differently in the thermoforming process when compared to an amorphous material. Ideal forming conditions; Mold temp. 170-190°F, Sheet temp. 320-360°F, part removal temp.145-170°F. Aluminum temperature controlled grit blasted tools are preferred. Ceramic tools can also work well if they are glass bead blasted. Quartz or ceramic heaters are preferred when working with Super Tuff-X 500. Calrod heaters can sometimes be used but gas fired is not recommended.

Finishing:
Super Tuff-X 500 can be fabricated by using many techniques such as; drilling, routing, punching, sawing, laser or die cut. Mechanical screws and other types of fasteners may be used to join Super Tuff-X 500 parts together. It may also be bonded with certain types of adhesives.

Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process.

Colors, Textures and Capabilities:
Our Super Tuff-X 500 material will accept any color. This product can also be painted with a two-part paint system. Super Tuff-X 500 is offered in gauges from .090 to .400 in. and in widths up to 120". Super Tuff-X 500 is offered in several different patterns that include; FL/HC, H/C, Diamond Plate, Smooth and Levant II.

General Information
Features	Good Chemical Resistance Good Colorability Good UV Resistance High Heat Resistance High Impact Resistance High Stiffness High Tensile Strength Low Temperature Impact Resistance Semi Crystalline
Uses	Automotive Applications Electrical/Electronic Applications Lawn and Garden Equipment Power/Other Tools Sporting Goods
Appearance	Colors Available
Forms	Sheet
Processing Method	Thermoforming

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.14	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)	0.50	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	26.0	MPa	ASTM D638
Flexural Modulus	2930	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-30°C	48	J/m
23°C	750	J/m
Instrumented Dart Impact (-30°C)	43.6	J	ASTM D3763

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	114	°C	ASTM D648
CLTE - Flow	4.0E-5	cm/cm/°C	ASTM D696

Flammability	Nominal Value		Test Method
Flame Rating (> 1.50 mm)	HB		UL 94

Additional Information	Nominal Value	Unit
De-mold Temperature	63 to 77	°C
Mold Temperature (other)	77 to 88	°C
Sheet Temperature	160 to 182	°C

Resin Grade	Manufacturer	Category	Trademark
RTP 1400 AG-330	RTP Company	PESU	RTP
WPP PP PPC3GF1.5UV-MS 428 Black	Washington Penn Plastic Co. Inc.	PP Copolymer	WPP PP
CONFOR® CF-47	E-A-R Specialty Composites	PUR, Unspecified	CONFOR®
POLIGOM G/30 C	Crosspolimeri S.p.A.	EPDM	POLIGOM
Kangxi® FRPC-10GF	Wuxi Kangxi Plastics Technology Co.,Ltd.	PC	Kangxi®