Boltaron 9815
| Category: | PMMA+PVC , Acrylic (PMMA) + PVC |
| Manufacturer: | Boltaron Performance Products |
| Trademark: | Boltaron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7vNaLC_Boltaron-9815.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Boltaron 9815 is a proprietary, fire retardant, press laminated thermoplastic sheet designed to meet stringent FAA requirements for flammability, smoke generation and heat release as set forth in FAR 25.853 paragraphs (a) and (d). Boltaron 9815 offers excellent impact strength, abrasion resistance, stain and chemical resistance, and superior thermoformability. Colors: Custom Gauges: .031 to .250 Sheet Sizes: 50"x99" & 55.5"x122" (untrimmed) Textures: Haircell Industrial Smooth Crush Falmuth Suede |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 to 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 40.0 to 44.1 | MPa | ASTM D638 |
| Flexural Modulus | 3030 to 3170 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 68.9 to 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 to 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 75.6 to 77.8 | °C | ASTM D648 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| FAA Flammability 1 | 12.0 60.0 | sec | FAR 25.853 |
| Heat Release 2 | FAR 25.853 | ||
| 2 Min-Hrr | < 65 | kW/m² | |
| Peak-Hrr | < 65 | kW/m² | |
| NBS Smoke Density | |||
| -- 3 | < 200 | ||
| -- 4 | < 100 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Forming Temperature | 168 to 185 | °C |
| Note Message | |
|---|---|
| 1 . | Pass |
| 2 . | A1 F, Part IV |
| 3 . | 4 Min, F814-84(b) |
| 4 . | 1.5 Min, F814-84(b) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SINOF P260T | SINOF HI-TECH MATERIAL CO. LTD | PPS | SINOF |
| Borlink™ LE0310-04 | Borealis AG | PE, Unspecified | Borlink™ |
| HiFill FR® PA6/6 GF25 FR-N IM | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |
| INFUSE™ 9010 | The Dow Chemical Company | OBC | INFUSE™ |
| LNP™ STAT-KON™ SC004 compound | SABIC Innovative Plastics Europe | Nylon 12 | LNP™ STAT-KON™ |