Sarlink® TPV X4750B42
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7uzA6A_Sarlink-TPV-X4750B42.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A highly engineered Thermoplastic Elastomer for use in demanding applications. Sarlink® X4750BLK42 is a black, low hardness UV stable grade possessing superior compression set, chemical resistance and high temperature performance. This product is a high flow material designed for injection molding applications that require superior flow properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.908 | g/cm³ | ASTM D792 |
| -- | 0.910 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A, 5 sec, Extruded | 50 | ||
| Shore A, 5 sec, Injection Molded | 53 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Across Flow : 100% Strain | 1.50 | MPa | |
| Flow : 100% Strain | 2.20 | MPa | |
| Tensile Strength | ASTM D412, ISO 37 | ||
| Across Flow : Break | 4.20 | MPa | |
| Flow : Break | 3.90 | MPa | |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Across Flow : Break | 440 | % | |
| Flow : Break | 320 | % | |
| Tear Strength - Across Flow | |||
| -- | 15.9 | kN/m | ASTM D624 |
| -- 1 | 16 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 15 | % | |
| 70°C, 22 hr | 26 | % | |
| 125°C, 70 hr | 40 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | -11 | % | ASTM D573, ISO 188 |
| 100% Strain, 135°C, 1000 hr | -1.0 | % | ASTM D573 |
| 150°C, 168 hr | -20 | % | ASTM D573, ISO 188 |
| 100% Strain, 150°C, 168 hr | -7.0 | % | ASTM D573 |
| 100% Strain 135°C, 1000 hr | -1.0 | % | ISO 188 |
| 100% Strain 150°C, 168 hr | -7.0 | % | ISO 188 |
| Change in Ultimate Elongation in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -1.0 | % | |
| 150°C, 168 hr | -13 | % | |
| Change in Durometer Hardness in Air | ASTM D573, ISO 188 | ||
| Shore A, 135°C, 1000 hr | 2.0 | ||
| Shore A, 150°C, 168 hr | -1.0 | ||
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 85 | % | ASTM D471, ISO 1817 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary @ 206/s | |||
| 200°C | 220 | Pa·s | ISO 11443 |
| 200°C | 220 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 177 to 216 | °C | |
| Middle Temperature | 177 to 216 | °C | |
| Front Temperature | 177 to 216 | °C | |
| Nozzle Temperature | 188 to 221 | °C | |
| Processing (Melt) Temp | 182 to 232 | °C | |
| Mold Temperature | 10.0 to 65.6 | °C | |
| Back Pressure | 0.0689 to 1.03 | MPa | |
| Screw Speed | 100 to 200 | rpm | |
| Screw L/D Ratio | 20.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 601 FR A | RTP Company | ABS | RTP |
| Tecolen® CP10 GR50 NL | Eurotec Engineering Plastics | PP Copolymer | Tecolen® |
| CALP 8803R | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Extir® CM Giotto 5 AE | Versalis S.p.A. | PS (EPS) | Extir® |
| Loyblend® TA-1300 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |