Lapex A G/30
| Category: | PESU , Polyethersulfone |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Lapex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7uusXD_Lapex-A-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyethersulphone (PES). UL94 V-0 classified, halogens free. Glass fibres. Low smoke density and low toxicity index. Very high dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 0.75 | % | |
| Flow : 2.00 mm | 0.30 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 9600 | MPa | |
| 60°C | 9400 | MPa | |
| 90°C | 9200 | MPa | |
| 120°C | 9000 | MPa | |
| 150°C | 9600 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 130 | MPa | |
| Break, 60°C | 125 | MPa | |
| Break, 90°C | 115 | MPa | |
| Break, 120°C | 100 | MPa | |
| Break, 150°C | 90.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.0 | % | |
| Break, 60°C | 2.1 | % | |
| Break, 90°C | 2.3 | % | |
| Break, 120°C | 2.4 | % | |
| Break, 150°C | 2.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 185 | °C | |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.0E-6 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Oxygen Index | 40 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 to 180 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 350 to 370 | °C | |
| Mold Temperature | 140 to 165 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ RC6G43-BK09 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |
| XYRON™ 640V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Nypol® PA A3 G50 HS RH PRTA012 NR439 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Baoding 67I74D | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Hostacom T 30 T2 | LyondellBasell Industries | PP Homopolymer | Hostacom |