Retpol® PDR 7813/2 UV2
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7sw8HN_Retpol-PDR-7813-2-UV2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Seblex PDR 7813/2 UV2 is an oil extended thermoplastic styrenic rubber modified polypropylene compound. It is a low flow extrusion grade developed for flexibility and low surface hardness to give it "soft- feel" characteristics. The material has been UV stabilized for intermittent exposure to UV radiation. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 2.00 mm | 85 | ||
| Shore A, 5 sec, 2.00 mm | 82 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% Strain, 2.00 mm | 5.00 | MPa | |
| 300% Strain, 2.00 mm | 6.50 | MPa | |
| Tensile Strength 2(Break, 2.00 mm) | 8.20 | MPa | ASTM D412 |
| Tensile Elongation 3(Break, 2.00 mm) | 450 | % | ASTM D412 |
| Tear Strength 4(2.00 mm) | 40.0 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 10 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 180 to 220 | °C | |
| Cylinder Zone 2 Temp. | 180 to 220 | °C | |
| Cylinder Zone 3 Temp. | 180 to 220 | °C | |
| Cylinder Zone 4 Temp. | 180 to 220 | °C | |
| Cylinder Zone 5 Temp. | 180 to 220 | °C | |
| Melt Temperature | 190 to 210 | °C | |
| Die Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | Die C, 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7450 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| CarmelStat™ CS 1200 | Carmel Olefins Ltd. | PP, Unspecified | CarmelStat™ |
| DIALAC® SE40 | UMG ABS, Ltd. | AES | DIALAC® |
| Geon™ Vinyl Rigid Extrusion L7416 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| LNP™ STAT-KON™ DX02437 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |