Generic PC - Proprietary
| Category: | PC , Polycarbonate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7s4GtQ_Generic-PC---Proprietary.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC - Proprietary This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.21 - 1.34 | g/cm³ | ASTM D792 |
| 23°C | 1.22 - 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.29 - 0.91 | % | ASTM D955 |
| Transverse flow : 23°C | 0.60 - 0.73 | % | ASTM D955 |
| 23°C | 0.40 - 0.75 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.090 - 0.16 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.12 - 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1860 - 2970 | MPa | ASTM D638 |
| 23°C | 2100 - 6470 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 47.0 - 65.8 | MPa | ASTM D638 |
| Yield, 23°C | 49.2 - 62.6 | MPa | ISO 527-2 |
| Fracture, 23°C | 44.7 - 91.0 | MPa | ASTM D638 |
| Fracture, 23°C | 43.0 - 90.7 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.9 - 6.9 | % | ASTM D638 |
| Yield, 23°C | 1.5 - 6.9 | % | ISO 527-2 |
| Fracture, 23°C | 1.4 - 21 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 23 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2040 - 3050 | MPa | ASTM D790 |
| 23°C | 2080 - 5240 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 86.2 - 145 | MPa | ASTM D790 |
| 23°C | 76.1 - 137 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 - 160 | J/m | ASTM D256 |
| 23°C | 5.1 - 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 340 - 2300 | J/m | ASTM D256 |
| 23°C | 20 - 180 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 2.96 - 45.3 | J | ASTM D3763 |
| 23°C | 2.04 - 128 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 134 - 144 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 114 - 152 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 122 - 144 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 125 - 142 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0 - 1.3E+7 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 5.1E+3 - 6.9E+6 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 298 - 299 | °C | |
| Middle Temperature | 315 - 316 | °C | |
| Front Temperature | 326 - 327 | °C | |
| Processing (Melt) Temp | 315 - 316 | °C | |
| Mold Temperature | 96.0 - 96.6 | °C | |
| Back Pressure | 0.258 - 0.265 | MPa | |
| Screw Speed | 45 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC - ProprietaryThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP331L | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Nanjing Hongrui PP P353 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| Borealis PP HD601CF | Borealis AG | PP Homopolymer | Borealis PP |
| FLEXCHEM™ 5553 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| INEOS HDPE T60-1200-119 | INEOS Olefins & Polymers USA | HDPE | INEOS HDPE |