Solef® 1006
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Solef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7o83Ge_Solef-1006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Solef® 1006 PVDF is a very low viscosity homopolymer resin mainly used in injection molding or in multifilament extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 to 40 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | < 0.040 | % | ASTM D570 |
| Mold Shrinkage - Linear | 2.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| Dynamic | 0.150 to 0.350 | ||
| Static | 0.200 to 0.400 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength - 2 m/s (23°C, 4.00 mm) | 25.0 to 75.0 | J/m | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crystallization Heat | 54.0 to 60.0 | J/g | ASTM D3417 |
| Crystallization Point | 137 to 144 | °C | ASTM D3418 |
| Heat of Fusion | 58.0 to 67.0 | J/g | ASTM D3417 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 1 sec, 2.00 mm) | 73 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 2.00 mm) | 1800 to 2600 | MPa | ASTM D638 |
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 50.0 to 60.0 | MPa | |
| Break, 23°C, 2.00 mm | 30.0 to 50.0 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 5.0 to 10 | % | |
| Break, 23°C, 2.00 mm | 20 to 300 | % | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-10 Wheel) | 5.00 to 10.0 | mg | ASTM D4060 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | ASTM D4065 |
| Vicat Softening Temperature | 135 to 145 | °C | ASTM D1525 3 |
| Melting Temperature | 170 to 175 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 134 to 144 | °C | ASTM D3418 |
| CLTE - Flow (0 to 40°C) | 1.4E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat | ASTM E968 | ||
| 23°C | 1200 | J/kg/°C | |
| 100°C | 1600 | J/kg/°C | |
| Thermal Conductivity (23°C) | 0.20 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 20 to 25 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1.00 mm, 1 kHz) | 7.00 to 10.0 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.100 mm) | V-0 | UL 94 | |
| Oxygen Index 4(3.00 mm) | 44 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| 4 . | Sheet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2505 A TFE 15 | RTP Company | PUR, Unspecified | RTP |
| THERMOLAST® K TF0STT (Series: FC/S) | KRAIBURG TPE | TPE | THERMOLAST® K |
| ACCUGUARD™ CP0467V2CSL | ACLO Compounders Inc. | PP Copolymer | ACCUGUARD™ |
| Petrothene® NA340013 | LyondellBasell Industries | LDPE | Petrothene® |
| Shida 020 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | SBS | Shida |