PLASTRON™ PP-GF50-02
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | PLASTRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7mq9vg_PLASTRON-PP-GF50-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLASTRON™ PP-GF50-02 is a Polypropylene material filled with 50% glass fiber. It is available in Asia Pacific. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 140 | MPa | ISO 527-2 |
| Flexural Modulus | 11500 | MPa | ISO 178 |
| Flexural Stress | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 162 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 180 to 230 | °C | |
| Middle Temperature | 190 to 240 | °C | |
| Front Temperature | 200 to 250 | °C | |
| Nozzle Temperature | 200 to 250 | °C | |
| Mold Temperature | 30.0 to 80.0 | °C | |
| Back Pressure | 5.00 to 10.0 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 A TFE 15 | RTP Company | Nylon 6 | RTP |
| Axiall PVC 6300 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Chemlon® E-66 GF15 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| CP PRYME® Polycarbonate PC100RULUV-10M Black | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| Hostacom X M2 U34 102942 | LyondellBasell Industries | PP Homopolymer | Hostacom |