Cheng Yu T890G3
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Cheng Yu Plastic Company Limited |
| Trademark: | Cheng Yu |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7l85RM_Cheng-Yu-T890G3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cheng Yu T890G3 is a Polybutylene Terephthalate (PBT) product filled with 30% glass fiber. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 to 0.70 | % | |
| Across Flow | 1.0 to 1.5 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength | 195 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 228 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Constant (60 Hz) | 3.70 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL GTX™ GTX902 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| Generic CPVC | Generic | CPVC | Generic |
| Jamplast JPPPO30GF | Jamplast, Inc. | PPE+PS | Jamplast |
| PETOPLEN EH 241 | PETKIM Petrokimya Holding A.S. | PP, Unspecified | PETOPLEN |
| Optix® CA-75 HID | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |