POCAN® DP 1105 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7kLIb8_POCAN-DP-1105-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, non-reinforced, injection molding, extrusion, improved flowability |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.31 | g/cm³ | ISO 1183 |
| Apparent Density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (250°C/1.2 kg) | 42.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 250°C, 2.00 mm 1 | 2.4 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | % | |
| Flow : 250°C, 2.00 mm 3 | 2.2 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.30 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 145 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2850 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 65.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 9.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 10 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 2750 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% Strain, 23°C | 80.0 | MPa | |
| 23°C 6 | 90.0 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 6.5 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GHMR, 07-030 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 110 | kJ/m² | |
| 23°C | 140 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 70 | kJ/m² | |
| 23°C | 80 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 185 | °C | ISO 306/B120 |
| Melting Temperature 8 | 223 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 1.0E-4 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.40 | ||
| 23°C, 1 MHz | 3.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.4E-3 | ||
| 23°C, 1 MHz | 0.022 | ||
| Comparative Tracking Index (Solution A) | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 700 | °C | IEC 60695-2-12 |
| Oxygen Index 9 | 25 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 250 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 2430 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Tenite™ Butyrate 485E3720016 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Sinpolene MBB1406 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| Electrafil® J-1305/CF/40 | Techmer Engineered Solutions | PPS | Electrafil® |
| SABIC® EPDM 657 | Saudi Basic Industries Corporation (SABIC) | EPDM | SABIC® EPDM |