Order Products : sales@su-jiao.com
PRE-ELEC® PE 1294
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7k5Yel_PRE-ELEC-PE-1294.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC®PE 1294 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PE 1294 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include large plastic parts like pallets, drums and containers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.996 | g/cm³ | ASTM D792 |
| -- | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 190°C/10.0 kg | 20 | g/10 min | |
| 190°C/2.16 kg | 2.0 | g/10 min | |
| 190°C/21.6 kg | 80 | g/10 min | |
| Molding Shrinkage - Flow | 1.5 to 2.5 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A | 95 | ||
| Shore D | 66 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 23.0 | MPa | ASTM D638, ISO 527-2 |
| -- | 12.0 | MPa | ASTM D638 |
| 4.00 mm | 12.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 15 | % | ASTM D638, ISO 527-2 |
| Break | 300 | % | ASTM D638 |
| Break, 4.00 mm | 300 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 1000 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 8.4 | kJ/m² | ASTM D256 |
| -20°C | 10 | kJ/m² | ISO 179 |
| 23°C | 15 | kJ/m² | ISO 179, ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 4.20 | kJ/m² | |
| 23°C, 4.00 mm | 12.6 | kJ/m² | |
| Notched Izod Impact Strength 3 | ISO 180 | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ||
| 23°C, 4.00 mm | No Break | ||
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 76.1 | °C | ASTM D648B |
| 0.45 MPa, Unannealed | 76.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 45.0 | °C | ASTM D648A, ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 125 | °C | ASTM D1525, ISO 306/A50 3 5 |
| -- | 62.8 | °C | ASTM D1525 6 |
| -- | 63.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+4 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 180 to 250 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 80.0 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN SFO-130A | Lotte Chemical Corporation | PP Homopolymer | RANPELEN |
| SUNFROST® KA75GA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| Westlake LLDPE LF1020 | Westlake Chemical Corporation | LLDPE | Westlake LLDPE |
| PEARLCOAT® 165K | Lubrizol Advanced Materials, Inc. | TPU-Polyether | PEARLCOAT® |
| LNP™ THERMOCOMP™ WF006H compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |