VALOX™ V8280 resin
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7hztGR_VALOX-V8280-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% GR PBT+PET. High stiffness. Excellent surface aesthetics. Applications include office furniture. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (266°C/5.0 kg) | 33 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.20 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 12800 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 145 | MPa | |
| Break | 145 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 2.2 | % | |
| Break | 2.2 | % | |
| Flexural Modulus 4(50.0 mm Span) | 10700 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 221 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 830 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 7.91 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 216 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 193 | °C | |
| Vicat Softening Temperature | 221 | °C | ASTM D1525 6 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 260 to 277 | °C | |
| Middle Temperature | 271 to 282 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Nozzle Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 282 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 P-45 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Ryton® R-4-02XT | Solvay Specialty Polymers | PPS | Ryton® |
| Globalprene® 1476F | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Epoxies, Ect. 10-3002 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| apilon 52® TL 25 NS | API SpA | TPU-Polyether | apilon 52® |