Surlyn Reflection Series® SURSG201UN

Category: Nylon 6 , Polyamide 6
Manufacturer: LTL Color Compounders, Inc.
Trademark: Surlyn Reflection Series®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: 7hwRbi_Surlyn-Reflection-Series-SURSG201UN.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
A patented alloy of DuPont™ Surlyn® resin and nylon 6 for applications that require a high gloss, molded in color surface finish directly from the mold.
General Information
Features
  • Good Colorability
  • High Gloss
Forms
  • Pellets
Processing Method
  • Injection Molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.04g/cm³ASTM D792
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)7.0g/10 minASTM D1238
Molding Shrinkage - Flow (3.18 mm)1.0%ASTM D955
MechanicalNominal ValueUnitTest Method
Tensile Strength 1ASTM D638
    Yield 40.3MPa
    Break 39.4MPa
Tensile Elongation 2ASTM D638
    Yield 11%
    Break 220%
Flexural Modulus 31140MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact ASTM D256
    -30°C 270J/m
    23°C 1500J/m
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)57.8°CASTM D648
InjectionNominal ValueUnit
Drying Temperature 60.0 to 62.8°C
Drying Time 6.0 to 8.0hr
Drying Time, Maximum 24hr
Suggested Shot Size 30 to 70%
Rear Temperature 241°C
Middle Temperature 241°C
Front Temperature 241°C
Processing (Melt) Temp 232 to 257°C
Mold Temperature 51.7 to 57.2°C
Back Pressure 0.345 to 0.689MPa
Vent Depth 0.025 to 0.038mm
Note Message
1 .51 mm/min
2 .51 mm/min
3 .51 mm/min
Resin Grade Manufacturer Category Trademark
RBW Reprocessed Extrusion Grade RBW Technologies, Inc. HDPE RBW
Braskem PP PH 0952 Braskem PP Homopolymer Braskem PP
Cheng Yu FV30710 Cheng Yu Plastic Company Limited Acetal (POM) Homopolymer Cheng Yu
Generic Biodeg Polymers Generic Biodeg Polymers Generic
Sylvin 8482-72 Black Sylvin Technologies Incorporated PVC+NBR Sylvin